WEICON F2 Epoxy Resin 2.0 kg

Composition

Epoxy resin aluminium-filled

Specific Properties

viscous

Colour after curing

aluminium

Density of the mixture (200g preparation)

1,45 g/cm3

Consumption at a coating thickness of

1,0 mm 1,45 kg/m2

Maximium layer thickness for each working step

10 mm

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

43 Mpa

Pull

14 Mpa

Bending

26 Mpa

E-Modul

1.500 to 2.000 Mpa

Shore D (ATSM D 1706)

79

Shrinkage

0,025 %

Tg after curing at room temperature

51,5 Tg ( deg C)

Tg after tempering (at 120 deg C)

53,1 Tg (deg C)

Thermoforming resistance

+55 deg C