WEICON Epoxy Resin HP 0-5 kg

Composition

Epoxy resin mineral-filled

Specific Properties

Pasty,  wear-resistant

Colour after curing

white

Density of the mixture (200g preparation)

1,48 g/cm3

Maximium layer thickness for each working step

10 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

30 min.

Handling strength at room temperature

16 h

Final hardness after

48 h

Tensile strength

21 Mpa

Elongation at break (DIN EN ISO 527)

6 %

Pressure

65 Mpa

Pull

21 Mpa

Bending

50 Mpa

Shore D (ATSM D 1706)

76

Linear shrinkage

0,02 %